Pulsed laser-assisted additive manufacturing of Ti-6Al-4V for in-situ grain refinement | Scientific Reports

2023-01-06 17:45:03 By : Ms. Apple Leung

Thank you for visiting nature.com. You are using a browser version with limited support for CSS. To obtain the best experience, we recommend you use a more up to date browser (or turn off compatibility mode in Internet Explorer). In the meantime, to ensure continued support, we are displaying the site without styles and JavaScript.

Carousel with three slides shown at a time. Use the Previous and Next buttons to navigate three slides at a time, or the slide dot buttons at the end to jump three slides at a time. Inconel 625 Plate

Pulsed laser-assisted additive manufacturing of Ti-6Al-4V for in-situ grain refinement | Scientific Reports

Zhongji Sun, Xipeng Tan, … Chee Kai Chua

Duyao Zhang, Dong Qiu, … Mark A. Easton

Philipp Kürnsteiner, Markus Benjamin Wilms, … Dierk Raabe

Xu Chen & Chunlei Qiu

Jie Ren, Yin Zhang, … Wen Chen

Jingqi Zhang, Yingang Liu, … Ming-Xing Zhang

Decheng Kong, Chaofang Dong, … Xiaogang Li

Pere Barriobero-Vila, Joachim Gussone, ... Guillermo Requena

Zhongji Sun, Yan Ma, … Dierk Raabe

Scientific Reports volume  12, Article number: 22247 (2022 ) Cite this article

Metal additive manufacturing (AM) enables rapid customization of complex parts. However, it leads to forming of columnar grain structures which give the AM parts anisotropic properties. In this study, we propose a pulsed laser-assisted AM (PLAAM) technique for in-situ grain refinement of Ti-6Al-4V parts. A nanosecond pulsed laser was focused onto a melt pool to generate a favorable environment for the promotion of fine equiaxed grains. The PLAAM technique provided an average prior-β grain size of 549.6 μm, compared to that of 1297 μm provided by the conventional AM technique. Moreover, the maximum value of multiples of uniform distribution of the β phase decreased from 16 to 7.7 when using the PLAAM technique, which indicates a weakened crystallographic texture. These changes confirm that the proposed PLAAM technique promotes finer and more equiaxed prior-β grains. Furthermore, because the proposed technique is a non-contact technique, it can be applied to existing processes without adjusting tool paths.

Metal additive manufacturing (AM) is a widely used layer-by-layer process for rapid prototyping and manufacturing of complex three-dimensional metallic structures1. However, the disadvantageous anisotropic tensile and fatigue properties of coarse columnar grain structures of AM parts inhibit the widespread use of AM in the manufacturing industry2,3. In typical AM processes, thermal gradients are steeply formed inside small melt pools, leading to strong epitaxial growth of columnar grains along the build direction2,3.

Among various metal AM materials, Ti-6Al-4V is the most researched material owing to its excellent applicability in the biomedical and aerospace industries1. However, because typical Ti-6Al-4V AM parts have coarse columnar prior-β grains, they exhibit anisotropic tensile properties1. Therefore, the promotion of fine equiaxed grains in AM parts has become an important research topic for improving their tensile properties3.

Various techniques have been proposed for introducing equiaxed grains in the AM parts. Introducing additional particles to assist active nucleation has been proven to be effective in promoting columnar-to-equiaxed transition, although changes in material composition are inevitable4,5,6. Post-processing techniques, such as inter-pass rolling7, machine hammer peening8, ultrasonic impact treatment9 and laser shock peening10,11, have also been proposed. However, because these techniques are applied after the solidification of layers, they require more processing time and might limit the complexity of the AM parts. Ultrasound-assisted AM resolves this problem by delivering high ultrasound energy to the melt pool12. However, an ultrasound transducer must be attached to the bottom of the base plate to efficiently deliver sufficient energy to agitate the melt pool. To apply this contact-type technique, implementation problems must be solved, because it is difficult to ensure stable effects on the moving melt pool with its three-dimensional trajectory. Recently, delivering localized ultrasound energy inside the melt pool via intensity-modulated laser irradiation was investigated for in-situ grain refinement13. As a proof of concept, the technique was verified on a stainless-steel plate, showing that the intensity-modulated laser can simultaneously perform surface melting and ultrasound generation. Meanwhile, a synchronous induction heating-assisted AM has been proposed recently for in-situ microstructural control. However, the task of stably applying the technique for arbitrary-shaped parts remains14.

In this study, we propose a pulsed laser-assisted AM (PLAAM) technique to refine the prior-β grains of Ti-6Al-4V parts during laser-directed energy deposition (DED). A nanosecond pulsed laser was incorporated into a DED system to deliver high pulsed energy to the melt pool during AM. Because PLAAM is an in-situ and non-contact technique that affects the melt pool, it can be applied to the AM of complex objects with arbitrary sizes and shapes. Inspired by the contact-type ultrasound technique12 and the well-established pulsed laser effects on liquids15, the proposed technique exploits laser-induced shock waves, cavitation, and accelerated Marangoni flow inside the melt pool to create a favorable environment for the formation of a fine equiaxed prior-β grain structure.

We experimentally demonstrate that the parts manufactured by PLAAM have finer and nearly equiaxed prior-β grain structures. In addition, we present a physical explanation of how the application of a pulsed laser can alter the prior β-grain structure of the deposited layers.

The PLAAM technique is illustrated in Fig. 1. To pinpoint the melt pool and directly deliver the pulsed laser energy during AM, the pulsed laser was focused onto the melt pool using a fiber-guided focal module attached to the DED nozzle. The focal module was fixed to the DED positioning frame so that the foci of the pulsed laser and DED laser coincided during AM. Although an off-axis configuration was adopted in this study, the pulsed laser can be coaxially designed with the DED laser using a dichroic mirror for full integration16.

Pulsed laser-assisted AM (PLAAM). (a) Off-axis configuration of a PLAAM system. (b) The pulsed laser induces shock waves, cavitation, and accelerated Marangoni flow inside the melt pool, providing a favorable environment for grain refinement.

The pulsed laser effects are illustrated in Fig. 1b. The wavelength and pulse duration of the pulsed laser were 532 nm and 10 ns, respectively. The focal size and pulse power density were selected as 2.8 × 10−3 cm2 and 0.41 GW/cm2, respectively, such that shock waves and cavitation could be generated inside the melt pool. With the given power density higher than the dielectric breakdown threshold of titanium, 0.36 GW/cm217, an avalanche process of ionization, also known as the dielectric breakdown, occurred in the melt pool with audible ablation sound and bright visible plasma sparks. These phenomena are known to be followed by plasma formation, shock wave propagation, and cavitation generation15. In addition, the selected pulsed laser parameter values were sufficient to accelerate the Marangoni flow inside the melt pool16. Change in the material composition was expected to be negligible because the laser ablation depth is in the order of the pulsed-laser wavelength (532 nm)15. A detailed explanation of these pulsed laser effects on the refinement of the prior-β grains is provided afterwards in the “Discussion” section.

The DED process parameters were selected to maintain a 250 μm target layer height during multilayer AM. With the chosen DED parameters, the energy density was calculated as 100 J/mm2, which can assure the total volume fraction of pores below 0.1%18. Because the averaged input power increased by the additional puled-laser excitation was only 1.15%, such small extra input power had little effect on the selection of the DED laser power. With a 300-mm/min scanning speed and a 100 Hz repetition rate of the pulsed laser, the distance between the two consecutive pulsed excitations during PLAAM was 50 μm. Because typical Ti-6Al-4V AM samples feature columnar prior-β grains of several millimeters in the building direction and several hundreds of micrometers in the scanning direction2,12, the given vertical (250 μm) and lateral (50 μm) excitation intervals were an order of magnitude smaller than the prior-β grain size. Thus, the pulsed laser could effectively alter the prior-β grain structure. Further study on optimizing the pulsed laser parameters is required to maximize grain refinement.

As shown in the optical microscopy (OM) images of Fig. 2a,b, the PLAAM sample exhibited finer and more equiaxed prior-β grains distributed over the entire build height of 30 mm, compared to the conventional AM sample with large columnar prior-β grains. The prior-β grain boundaries were manually traced for further analysis using the ImageJ software19. The number of prior-β grains per unit area of the PLAAM sample (6.91 mm−2) was 3.78 times that of the conventional AM sample (1.83 mm−2), meaning that the PLAAM sample had finer prior-β grains. In addition, the lengths and aspect ratios of the prior-β grains are presented in histograms to statistically show the changes in the grain structure (see Fig. 2c,d). Using the PLAAM technique, the mean length of the prior-β grains decreased from 1297 to 549.6 μm, and the mean aspect ratio decreased from 3.5 to 2.5. Moreover, the variation in the prior-β grain size and shape was smaller using PLAAM than with conventional AM. These results indicate that the PLAAM sample exhibits finer equiaxed prior-β grains than the conventional AM sample.

Change in prior-β grain structure. OM images along the build direction of conventional AM (a) and PLAAM (b) samples. z and x are the build and transverse directions, respectively. Histograms of the length (c) and aspect ratio (d) of the prior-β grains observed in (a) and (b). The overlapped histograms are shown in a darker color.

For a closer inspection of the prior-β grains, electron backscatter diffraction (EBSD) analysis was conducted on the samples, as shown in Fig. 3. The inverse pole figure maps for the β phase (Fig. 3a,c) show that the PLAAM sample had a nearly equiaxed prior-β grain structure, compared to the conventional AM sample with a columnar prior-β grain structure along the build direction. The inverse pole figure maps were reconstructed using an open-source MATLAB toolbox MTEX20. Contoured pole figures for the β phase of the two samples (Fig. 3b,d) were also calculated to quantitatively visualize the texture change with multiples of uniform distribution (MUD) values. The PLAAM sample had a maximum MUD of 7.7, which was less than half that of the conventional AM sample (16). Compared to a strong crystallographic texture in the < 001 > direction shown in the AM sample, a weak texture is observed in the PLAAM sample. These results confirm that the PLAAM sample had a more isotropic structure of finer prior-β grains compared to the conventional AM sample.

EBSD analysis of the conventional AM (a, b) and PLAAM (c, d) samples. Inverse pole figure maps for the β phase along the build direction (a, c). Contoured pole figures for the β phase (b, d). z and (x,y) are the build direction and transversal plane, respectively.

The pulsed laser parameters were chosen to (1) accelerate the Marangoni flow in the melt pool by instantaneous and localized heating on the surface16; (2) generate shock waves; and (3) create cavitations in the melt pool following dielectric breakdown15. Here we discuss how these effects enhance equiaxed nucleation in the melt pool. Equiaxed nucleation can be promoted by increasing constitutional supercooling21. To increase constitutional supercooling, either the melting temperature should be increased, or the thermal gradient should be decreased.

The melting temperature can be increased by high-pressure shock waves impinging on the melt pool. Based on the Clausius–Clapyron equation, the relationship between the melting temperature elevation and pressure change can be expressed as follows:

where \({\textit{T}}_{{\text{m}}}\) is the melting temperature (K), \({\textit{P}}\) is the pressure (Pa), \({\textit{V}}\) is the volume change upon melting (m3), and \({\textit{H}}\) is the latent heat of fusion (J/kg). Based on Eq. (1) and the material properties of Ti-6Al-4V summarized in Table 1, a shock pressure of 100 MPa produced by cavitation22, for example, leads to a melting-temperature increase of 8.66 K. Moreover, with a power density of 0.41 GW/cm2, the pulsed-laser-induced shock waves impinged upon the melt pool create pressures up to 336.2 MPa according to Lindl’s Equation23,24:

where P is the generated shock pressure (GPa), I is the laser power density (1015 W/cm2), and λ is the wavelength of the laser (μm). This high pressure leads to a melting-temperature increase of 29.31 K. This increase in the melting temperature is directly translated to the increase in constitutional supercooling25. With increased constitutional supercooling, initial nuclei are likely to be activated near the cavitations and shock wave fronts. These events can suppress the epitaxial growth of columnar grains by competition. Previous works have experimentally demonstrated a similar mechanism using ultrasound-induced cavitations to promote equiaxed nucleation in welding25 and in AM12,21. The performance of PLAAM can be compared to a recent study26 about alloying yttria-stabilized zirconia (YSZ) for grain-refined AM of Ti-6Al-4V. The authors showed that adding 5% YSZ to Ti-6Al-4V increased constitutional supercooling by 112 K and decreased the average length of the prior-β grains from > 2 mm to 118 μm.

In PLAAM, the pulsed laser effects further increased constitutional supercooling by decreasing the thermal gradient inside the melt pool. Because of the opposing directions of the Marangoni flow and pulsed laser-induced shock waves as illustrated in Fig. 1b, a vigorous turbulent flow is created inside the melt pool16. Moreover, cavitation-induced shock waves generate sporadic and instantaneous turbulence inside the melt pool. In this environment, nuclei activated by increased constitutional supercooling are distributed in the melt pool. Hence, the epitaxial growth of large columnar prior-β grains is further subjected to competition.

In summary, we have demonstrated in-situ grain refinement of Ti-6Al-4V parts using a hybrid AM technique named as PLAAM. The proposed technique exploits a high-power-density pulsed laser to create a favorable environment for the growth of equiaxed prior-β grains. Because the technique is a non-contact type, it can be applied to any existing AM equipment without adjusting the arbitrary tool path. Microstructural assessments show that the PLAAM sample has smaller and more equiaxed prior-β grains compared to the conventional AM sample having large columnar prior-β grains. Also, the maximum value of MUD of the β phase decreased from 16 to 7.7 when using the PLAAM technique, indicating a weakened texture and refined prior-β grains. A detailed explanation of the pulsed laser effects on the melt pool is also presented for further adaptation of the proposed approach. Because the equiaxed prior-β grain structure is known for its isotropic and high tensile properties, the proposed technique is expected to be extensively studied for producing high-quality metal AM parts.

A Q-switched Nd:YAG pulsed laser (Centurion+, Quantel) was incorporated into a laser metal powder DED system (MX-400, InssTek) equipped with a continuous-wave Yb-fiber DED laser, as illustrated in Fig. 1a. The working distances of the pulsed laser and DED laser were 43 mm and 9 mm, respectively. The power and focal diameter of the DED laser, powder feed rate, and flow rate of coaxial argon gas were set to 100 W, 800 μm, 1 g/min, and 6.0 L/min, respectively.

Walls with dimensions of 30 × 30 × 1.3 mm (height × width × thickness) made of 120 layers were fabricated by both the conventional AM and PLAAM techniques. Commercial-grade 23 Ti-6Al-4V powder (AP&C) with a diameter ranging from 45 to 150 μm was used to deposit the layers. The samples were separated from the substrate for post-fabrication grain structure inspection. The samples were polished and etched using a Kroll’s etchant (4 mL of HF, 6 mL of HNO3, and 90 mL of H2O). The structure and shape of the prior-β grains were examined via OM (Stemi 508, ZEISS). The microstructure texture was examined by EBSD using a detector (QUANTAX EBSD, Bruker) operated with an acceleration voltage of 20 kV and a step size of 4.2 μm.

The datasets used and/or analyzed during the current study are available from the corresponding author upon reasonable request.

Herzog, D., Seyda, V., Wycisk, E. & Emmelmann, C. Additive manufacturing of metals. Acta Mater. 117, 371–392 (2016).

Article  ADS  CAS  Google Scholar 

Carroll, B. E., Palmer, T. A. & Beese, A. M. Anisotropic tensile behavior of Ti–6Al–4V components fabricated with directed energy deposition additive manufacturing. Acta Mater. 87, 309–320 (2015).

Kok, Y. et al. Anisotropy and heterogeneity of microstructure and mechanical properties in metal additive manufacturing: A critical review. Mater. Des. 139, 565–586 (2018).

Choi, G., Choi, W. S., Han, J. & Choi, P. P. Additive manufacturing of titanium-base alloys with equiaxed microstructures using powder blends. Addit. Manuf. 36, 101467 (2020).

Liao, Y., Bai, J., Chen, F., Xu, G. & Cui, Y. Microstructural strengthening and toughening mechanisms in Fe-containing Ti-6Al-4V: A comparison between homogenization and aging treated states. J. Mater. Sci. Technol. 99, 114–126 (2022).

Xiong, Z., Pang, X., Liu, S., Li, Z. & Misra, R. D. K. Hierarchical refinement of nickel-microalloyed titanium during additive manufacturing. Scr. Mater. 195, 113727 (2021).

Donoghue, J. et al. The effectiveness of combining rolling deformation with Wire-Arc Additive Manufacture on β-grain refinement and texture modification in Ti–6Al–4V. Mater. Charact. 114, 103–114 (2016).

Hönnige, J. R. et al. The effectiveness of grain refinement by machine hammer peening in high deposition rate wire-arc AM Ti-6Al-4V. Metall. Mater. Trans. A 51, 3692–3703 (2020).

Wang, Y. & Shi, J. Recrystallization behavior and tensile properties of laser metal deposited Inconel 718 upon in-situ ultrasonic impact peening and heat treatment. Mater. Sci. Eng. A 786, 139434 (2020).

Lu, J. et al. High-performance integrated additive manufacturing with laser shock peening–induced microstructural evolution and improvement in mechanical properties of Ti6Al4V alloy components. Int. J. Mach. Tools Manuf. 148, 103475 (2020).

Lan, L., Jin, X., Gao, S., He, B. & Rong, Y. Microstructural evolution and stress state related to mechanical properties of electron beam melted Ti-6Al-4V alloy modified by laser shock peening. J. Mater. Sci. Technol. 50, 153–161 (2020).

Todaro, C. J. et al. Grain structure control during metal 3D printing by high-intensity ultrasound. Nat. Commun. 11, 142 (2020).

Article  ADS  CAS  Google Scholar 

Ivanov, I. A. et al. Effect of laser-induced ultrasound treatment on material structure in laser surface treatment for selective laser melting applications. Sci. Rep. 11, 23501 (2021).

Article  ADS  CAS  Google Scholar 

Fan, W. et al. Overcoming the limitation of in-situ microstructural control in laser additive manufactured Ti–6Al–4V alloy to enhanced mechanical performance by integration of synchronous induction heating. J. Mater. Sci. Technol. 94, 32–46 (2021).

Kennedy, P. K., Hammer, D. X. & Rockwell, B. A. Laser-induced breakdown in aqueous media. Prog. Quantum Electron. 21, 155–248 (1997).

Article  ADS  CAS  Google Scholar 

Sohn, H. et al. Real-time porosity reduction during metal directed energy deposition using a pulse laser. J. Mater. Sci. Technol. 116, 214–223 (2022).

Petzoldt, S., Reif, J. & Matthias, E. Laser plasma threshold of metals. Appl. Surf. Sci. 96, 199–204 (1996).

Kasperovich, G., Haubrich, J., Gussone, J. & Requena, G. Correlation between porosity and processing parameters in TiAl6V4 produced by selective laser melting. Mater. Des. 105, 160–170 (2016).

Schneider, C. A., Rasband, W. S. & Eliceiri, K. W. NIH Image to ImageJ: 25 years of image analysis. Nat. Methods 9, 671–675 (2012).

Bachmann, F., Hielscher, R. & Schaeben, H. Texture analysis with MTEX–free and open source software toolbox. Solid State Phenom. 160, 63–68 (2010).

Todaro, C. J. et al. Grain refinement of stainless steel in ultrasound-assisted additive manufacturing. Addit. Manuf. 37, 101632 (2021).

Zhong , X. , Eshraghi , J. , Vlachos , P. , Dabiri , S. & Ardekani , AM A model for a laser-induced cavitation bubble .Int.J. Multiph.Flow 132, 103433 (2020).

Article  MathSciNet  CAS  Google Scholar 

Schneider, M. S. et al. Laser-induced shock compression of copper: Orientation and pressure decay effects. Metall. Mater. Trans. A Phys. Metall. Mater. Sci. 35, 2633–2646 (2004).

Lindl, J. Development of the indirect-drive approach to inertial confinement fusion and the target physics basis for ignition and gain. Phys. Plasmas 2, 3933–4024 (1995).

Article  ADS  CAS  Google Scholar 

Yuan, T., Kou, S. & Luo, Z. Grain refining by ultrasonic stirring of the weld pool. Acta Mater. 106, 144–154 (2016).

Article  ADS  CAS  Google Scholar 

Choi, G. et al. Decomposition behavior of yttria-stabilized zirconia and its effect on directed energy deposited Ti-based composite material. J. Mater. Sci. Technol. 112, 138–150 (2022).

Zhang, T. et al. Evolution of molten pool during selective laser melting of Ti–6Al–4V. J. Phys. D Appl. Phys. 52, 055302 (2018).

This work was supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government (MSIT) [Grant Number 2019R1A3B3067987]. H.Y. was supported by SQ Engineering during his stay at KAIST.

Present address: Tomocube, Daejeon, 34109, Republic of Korea

Present address: Analysis Solution Center, SK Innovation, 34124, Daejeon, Republic of Korea

Global R&D Center, SQ Engineering, Seoul, 05818, Republic of Korea

Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology (KAIST), Daejeon, 34141, Republic of Korea

Hansol Yoon, Peipei Liu & Hoon Sohn

Center for 3D Printing Nondestructive Testing, KAIST, Daejeon, 34141, Republic of Korea

Peipei Liu & Hoon Sohn

Department of Materials Science and Engineering, KAIST, Daejeon, 34141, Republic of Korea

Yejun Park, Gwanghyo Choi & Pyuck-Pa Choi

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

You can also search for this author in PubMed  Google Scholar

H.Y., P.L. and H.S. conceived the experiments. H.Y. and P.L. conducted the experiments. H.Y. established the grain refinement mechanism. Y.P. and G.C. performed the EBSD analysis. H.Y., P.L., Y.P. and G.C. performed all the remaining analyses. H.Y. prepared Figs. 1 and 2. H.Y. and Y.P. prepared Fig. 3. P.P.C. supervised all the analyses. H.S. supervised the entire project. H.Y. wrote the manuscript with all co-authors’ contributions.

H.Y. was supported by SQ Engineering during his stay at KAIST. The remaining authors declare no competing interests.

Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.

Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.

Yoon, H., Liu, P., Park, Y. et al. Pulsed laser-assisted additive manufacturing of Ti-6Al-4V for in-situ grain refinement. Sci Rep 12, 22247 (2022). https://doi.org/10.1038/s41598-022-26758-y

DOI: https://doi.org/10.1038/s41598-022-26758-y

Anyone you share the following link with will be able to read this content:

Sorry, a shareable link is not currently available for this article.

Provided by the Springer Nature SharedIt content-sharing initiative

By submitting a comment you agree to abide by our Terms and Community Guidelines. If you find something abusive or that does not comply with our terms or guidelines please flag it as inappropriate.

Scientific Reports (Sci Rep) ISSN 2045-2322 (online)

Pulsed laser-assisted additive manufacturing of Ti-6Al-4V for in-situ grain refinement | Scientific Reports